Selective sensing performance of mesoporous carbon nitride with a highly ordered porous structure prepared from 3-amino-1,2,4-triazine
Journal article   Peer reviewed

Selective sensing performance of mesoporous carbon nitride with a highly ordered porous structure prepared from 3-amino-1,2,4-triazine

G P Mane, D S Dhawale, C Anand, K Ariga, Q Ji, Mohammad A Wahab, T Mori and A Vinu
Journal of Materials Chemistry A, Vol.1(8), pp.2913-2920
2013
DOI: https://doi.org/10.1039/c2ta01215d
url
https://doi.org/10.1039/c2ta01215dView
Published Version

Abstract

We demonstrate the preparation of highly ordered and graphitic mesoporous carbon nitride with an ordered porous structure and a high nitrogen content (MCN-ATN) by a nano-hard-templating approach through a simple polymerization of 3-amino-1,2,4-triazine (ATN) inside the pore channels of a mesoporous silica template with an Ia3d symmetry and a 3D porous structure. Powder X-ray diffraction and high resolution transmission electron microscopy analysis show that the prepared materials exhibit well-ordered mesopores with a 3D porous network. Nitrogen adsorption measurements also confirm that the samples possess excellent physical parameters including high surface areas (472-635 m2 g-1), large pore volumes (0.71-0.99 cm3 g-1) and tunable pore diameters (5.5-6.0 nm). One of the most important features of this work is that the cyclic aromatic precursor helps to preserve the nitrogen in the carbon matrix of the final product even after the carbonization process. The C/N ratio of the samples is ca. 0.92 which is much lower than that obtained for the samples prepared using ethylene diamine and carbon tetrachloride through a nano-hard templating process. X-ray photoelectron spectroscopy results reveal that MCN-ATN is mainly composed of sp2 hybridized carbon atoms bonded with nitrogen atoms, associated with the triazine moieties from the ATN molecules. Temperature programmed desorption of CO2 over MCN-ATN demonstrates that the sample is basic which originates from the amine groups on the surface of the CN wall structure. Finally, the samples are mounted on the quartz crystal microbalance (QCM) and used for sensing both acidic and basic organic vapors. Among the samples studied, MCN-ATN with the largest pore diameter showed a highly selective sensing performance for acidic molecules, especially the formic acid thanks to the presence of weak basic sites on the CN walls.

Details

Metrics

195 Record Views
100 Times Cited - Web of Science

InCites Highlights

These are selected metrics from InCites Benchmarking & Analytics tool, related to this output

Collaboration types
Domestic collaboration
International collaboration
Web Of Science research areas
Chemistry, Physical
Energy & Fuels
Materials Science, Multidisciplinary
Logo image